The effect of heat treatment on microstructure and mechanical properties of the Ti-steel explosive-rolling clad plate was elaborated by optical microscopy （OM）, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM）, micro-hardness test and shear test. The composites were subjected to heat treatment at temperature of 650-950 ~C for 60 min. The results show that the heat treatment process results in a great enhancement of diffusion and microstructural transformation. The shear strength decreases as the treatment temperature increases. Heated at 850 ℃ or below, their shear strength decreases slowly as a result of the formation of TiC in the diffusion interaction layer; while at the temperature of 850 ℃ or above, the shear strength decreases obviously, which is the consequence of a large amount of Ti-Fe intermetaUics （Fe2Ti/FeTi） along with some TiC distributing continuously at diffusion reaction layer.
通过室温压缩试验,研究全片层γ-TiAl基合金在不同加载速度和不同卸载载荷下的压缩断裂行为。结果表明:随着加载速度的增加,γ-TiAl基合金试样的屈服强度及抗压强度相应增大;试样的最终断裂是通过裂纹的形核、扩展以及相互贯通而形成的,断裂面主要由剪应力形成的撕裂区和压应力形成的解理断裂区域组成,并且在不同加载速度下,断口也呈现出规律性的变化。在不同载荷加载-卸载-再加载的过程中,小载荷(4.67、9.42、18.94 k N)下卸载和加载的名义应力-名义应变曲线完全重合,大载荷(26.60、37.24、53.20 k N)下卸载后产生的不可逆应变依次增大;裂纹面密度随着卸载载荷的增大而逐渐增大,材料的损伤程度不断增加。